ASTM A691/A691M-18 pdf free download. Standard Specification for Carbon and Alloy Steel Pipe, Electric-Fusion-Welded for High-Pressure Service at High Temperatures.
ASTM A691/A691M-18 covers carbon and alloy steel pipe, electric-fusion-welded with filler metal added, fabricated from pressure-vessel-quality plate of several analyses and strength levels and suitable for high-pressure service at high temperatures. Heat treatment may or may not be required to attain the desired mechanical properties or to comply with applicable code requirements. Supplementary requirements are provided for use when additional testing or examination is desired.
The values stated in either SI units or inch-pound units are to be regarded separately as standard. Within the text, the SI units are shown in brackets. The values stated in each system may not be exact equivalents: therefore, each system hall be used independently of the other. Combining values from the two systems may result in non-conformance with the standard. The inch-pound units shall apply unless the “M designation of this specification is specified in the order.
6. General Requirements
6.1 Material furnished to this specification shall conform to the applicable requirements of the current edition of Specifi cation A530/A530M, unless otherwise provided herein.
7. Chemical Requirements
7. 1 Product Analysis of Plate-The pipe manufacturer shall make an analysis of each mill heat of plate material. The product analysis so determined shall meet the requirements of the plate specification to which the material was ordered
7.2 Product Analysis of Weld-The pipe manufacturer shall make an analysis of finished deposited weld metal from each 200 ft [60 m] or fraction thereof. Analysis shall conform to the welding procedure for deposited weld metal.
7.3 Analysis may be taken from the mechanical test speci mens. The results of the analyses shall be reported to the purchaser.
5. Materials and Manufacture
5. 1 Materials-The steel plate material shall conform to the requirements of the applicable plate specification for the pipe grade ordered as listed in Table I
5.2 Welding.
5. 2. I The joints shall be double-welded full-penetration welds made in accordance with procedures and by welders or welding operators qualified in accordance with the ASME Boiler and Pressure Vessel Code,Section IX.
5.2.2 The welds shall be made either manually or automatically by an electric process involving the deposition of filler metal.

                                           Information                                             Download
PS:                           Due to copyright issues, Most documents cannot be downloaded.All contents are for personal learning only.
ASTM D2939-98 pdf download ASTM Standards

ASTM D2939-98 pdf download

ASTM D2939-98 pdf free download.Standard Test Methods for Emulsified Bitumens Used as Protective Coatings. ASTM D2939-98 covers procedures for sampling and testing emulsified bitumens used in relatively thick films as protective coatings for metals and built-up roofs....
Download Now
ASTM C94/C94M-15a pdf download ASTM Standards

ASTM C94/C94M-15a pdf download

ASTM C94/C94M-15a pdf free download.Standard Specification for Ready-Mixed Concrete. ASTM C94/C94M-15a covers ready-mixed concrete as defined in 3.2.2 (Note 1). Requirements for quality of ready-mixed concrete shall be either as stated in this specification or as ordered...
Download Now
ASTM D56-16 pdf download ASTM Standards

ASTM D56-16 pdf download

ASTM D56-16 pdf free download. Standard Test Method for Flash Point by Tag Closed Cup Tester. To ensure an acceptable precision, this dynamic flash point test method employs a prescribed rate of’ temperature rise for the material...
Download Now

LEAVE A REPLY

Anonymous netizen Fill in information